Achieving zT > 1 in Inexpensive Zintl Phase Ca_9Zn_(4+x)Sb_9 by Phase Boundary Mapping

  • 1. ROR icon California Institute of Technology
  • 2. ROR icon Northwestern University
  • 3. ROR icon Dalhousie University
  • 4. ROR icon Jet Propulsion Lab
  • 5. ROR icon Michigan State University

Abstract

Complex multinary compounds (ternary, quaternary, and higher) offer countless opportunities for discovering new semiconductors for applications such as photovoltaics and thermoelectrics. However, controlling doping has been a major challenge in complex semiconductors as there are many possibilities for charged intrinsic defects (e.g., vacancies, interstitials, antisite defects) whose energy depends on competing impurity phases. Even in compounds with no apparent deviation from a stoichiometric nominal composition, such defects commonly lead to free carrier concentrations in excess of 10^(20) cm^(−3). Nevertheless, by slightly altering the nominal composition, these defect concentrations can be tuned with small variation of the chemical potentials (composition) of each element. While the variation of chemical composition is undetectable, it is shown that the changes can be inferred by mapping (in nominal composition space) the boundaries where different competing impurity phases form. In the inexpensive Zintl compound Ca_9Zn_(4+x)Sb_9, the carrier concentrations can be finely tuned within three different three-phase regions by altering the nominal composition (x = 0.2–0.8), enabling the doubling of thermoelectric performance (zT). Because of the low thermal conductivity, the zT can reach as high as 1.1 at 875 K, which is one of the highest among the earth abundant p-type thermoelectrics with no ion conducting.

Additional Information

© 2017 Wiley-VCH Verlag GmbH & Co. KGaA, Weinheim. Received: December 2, 2016; Revised: February 3, 2017; Published online: March 29, 2017. This work was supported by the NASA Science Mission Directorate's Radioisotope Power Systems Thermoelectric Technology Development. S.O. acknowledges the financial assistance of Japan Student Service Organization (JASSO) and would like to thank Stephen Dongmin Kang and Max Wood for the helpful discussions. M.A.W. acknowledges the support of NSERC and the Materials Characterization Facilities at Dalhousie University's Institute for Research in Materials. J.-H.P. is grateful to the NSERC CREATE DREAMS (Dalhousie Research in Energy, Advanced Materials and Sustainability program) for funding. M.A. acknowledges the support from the Novartis Universität Basel Excellence Scholarship for Life Sciences and the Swiss National Science Foundation (Grant No. P300P2-158407). C.W. (DFT calculations) acknowledges the support from the DOE (Grant No. DE-FG02-07ER46433). The Swiss National Supercomputing Center in Lugano (Project s499, s621, and s700), the Extreme Science and Engineering Discovery Environment (XSEDE) (which was supported by the National Science Foundation Grant No. OCI-1053575), the Bridges system at the Pittsburgh Supercomputing Center (PSC) (which was supported by the NSF Award No. ACI-1445606), and the National Energy Research Scientific Computing Center (DOE: DE-AC02-05CH11231), are gratefully acknowledged.

Attached Files

Supplemental Material - adfm201606361-sup-0001-S1.pdf

Files

adfm201606361-sup-0001-S1.pdf

Files (1.4 MB)

Name Size
md5:fc1b37ac64622e439dd8a353975aee64
1.4 MB Preview Download

Additional details

Additional titles

Alternative title
Achieving zT > 1 in Inexpensive Zintl Phase Ca9Zn4+xSb9 by Phase Boundary Mapping

Identifiers

Eprint ID
75519
DOI
10.1002/adfm.201606361
Resolver ID
CaltechAUTHORS:20170329-142514472

Funding

NASA
Japan Student Service Organization (JASSO)
Natural Sciences and Engineering Research Council of Canada (NSERC)
Dalhousie University
Novartis Universität
Swiss National Science Foundation (SNSF)
P300P2-158407
Department of Energy (DOE)
DE-FG02-07ER46433
NSF
OCI-1053575
NSF
ACI-1445606
Department of Energy (DOE)
DE-AC02-05CH11231

Dates

Created
2017-03-29
Created from EPrint's datestamp field
Updated
2021-11-15
Created from EPrint's last_modified field