Hydrogenation of Magnesium Nickel Boride for Reversible Hydrogen Storage

We report that a ternary magnesium nickel boride (MgNi_(2.5)B_2) mixed with LiH and MgH_2 can be hydrogenated reversibly forming LiBH_4 and Mg_2NiH_4 at temperatures below 300 °C. The ternary boride was prepared by sintering a mechanically milled mixture of MgB_2 and Ni precursors at 975 °C under inert atmosphere. Hydrogenation of the ternary, milled with LiH and MgH_2, was performed under 100 to 160 bar H_2 at temperatures up to 350 °C. Analysis using X-ray diffraction, Fourier transform infrared, and ^(11)B magic angle spinning NMR confirmed that the ternary boride was hydrogenated forming borohydride anions. The reaction was reversible with hydrogenation kinetics that improved over three cycles. This work suggests that there may be other ternary or higher order boride phases useful for reversible hydrogen storage.